Effects of Prior Aging at Elevated Temperature in Air and in Argon Environments on Creep Response of PMR-15 Neat Resin at 288°C (Paperback) (ISBN-13: 9781288289776)

Creep behavior of PMR-15 neat resin, a polyimide thermoset polymer, aged in air or argon gaseous environments at 288-C for up to 1000 h was evaluated. Creep tests were performed at 288-C at creep stress levels of 20 and 10 MPa. Creep periods of at least 25 h in duration were followed by recovery at zero stress. Weight loss and growth of the oxidation layer were also monitored and correlated with aging time. The aging time in both air and argon environments had a strong influence on the creep and recovery response of PMR-15 neat resin. Samples aged in argon for 1000 h and tested at a creep stress level of 20 MPa produced creep strain of 4%, while the as-processed samples accumulated creep strain of 16%. DMA tests were performed to examine any changes in the glass transition temperature (Tg) of the PMR-15 neat resin. DMA results revealed an increase in (Tg) from 331-C to 336.5-C after 1000 h in argon at 288-C. Increase in Tg, indicating an increase in crosslink density due to aging in both air and argon environments is likely behind the changes in elastic modulus and in creep and recovery behavior.

This work has been selected by scholars as being culturally important, and is part of the knowledge base of civilization as we know it. This work was reproduced from the original artifact, and remains as true to the original work as possible. Therefore, you will see the original copyright references, library stamps (as most of these works have been housed in our most important libraries around the world), and other notations in the work.

This work is in the public domain in the United States of America, and possibly other nations. Within the United States, you may freely copy and distribute this work, as no entity (individual or corporate) has a copyright on the body of the work.

As a reproduction of a historical artifact, this work may contain missing or blurred pages, poor pictures, errant marks, etc. Scholars believe, and we concur, that this work is important enough to be preserved, reproduced, and made generally available to the public. We appreciate your support of the preservation process, and thank you for being an important part of keeping this knowledge alive and relevant.